Shanghai GongYe offers 3 standard grades of spun ceramic fiber blanket, all of which are lightweight and thermally efficient, resulting in a material that possesses the advantages of low heat storage and complete resistance to thermal shock. Used in a variety of heat processing applications, the ceramic fiber blanket is produced from high strength spun ceramic fibers and is needled to provide exceptional handling strength. The ceramic fiber blanket is completely inorganic and is available in a variety of densities, thicknesses, widths and temperature ratings:
Commercial grade: service temperature 1800°F High-Purity grade: service temperature 2300 °F Zirconia grade: service temperature 2600 °F Standard Densities: 6, 8 Ibs./cu. ft. (96, 128 kg/m3) Standard Thicknesses: 1/2", 1", 1-1/2",2" Standard Widths: 24" and 48" Standard Packaging: Cartons or bags
Note: Other densities available per special request
Features of Ceramic Fiber Blanket:
Furnace repair
Furnace, kiln, reformer and boiler linings
Furnace door linings and seals
Reusable insulation for steam and gas turbines
High-temperature kiln and furnace insulation
Primary reformer heater insulation
High temperature gasketing
Expansion joint seals
Glass furnace crown insulation
Field steam generator lining
Nuclear insulation applications
Thermal reactor insulation
Flexible high temperature pipe insulation
Investment casting mold wrapping
Removable casting mold wrapping
Removable insulating blankets for stress relieving welds
Pressure and cryogenic vessel fire protection
Soaking pit seals
High temperature filtration
Incineration equipment and stack linings
Spun Ceramic Fiber Blanket Physical Properties
Ceramic Blanket Specs
Commercial Grade Blanket
High-Purity Grade Blanket
Zirconia
Grade Blanket
Color
White
White
White
Maximum Use Limit
1260°C (2300°F)
1260°C (2300°F)
1426°C (2600°F)
Continuous Use Limit
800°C (1472°F)
1100°C (2012°F)
1350°C (2461°F)
Average Fiber Diameter
3 - 4.5 microns
3 - 4.5 microns
3 - 4.5 microns
Average Tensile Strength
4 pcf. density
6 pcf. density
8 pcf. density
5.075 psi
7.250 psi
11.600 psi
5.075 psi
7.250 psi
11.600 psi
5.075 psi
7.250 psi
11.600 psi
Rate of Linear Shrinkage
(24 hrs @ 1000°C)
(24 hrs @ 1100°C)
(24 hrs @1200°C )
(24 hrs @ 1350°C )
4%
-
-
-
-
3%
-
-
-
-
-
3%
Thermal Conductivity w/m-k (Btu in./hr/ft2°F)
4 pcf. density @ 400°C (752°F)
4 pcf. density @ 600°C (1112°F)
4 pcf. density @ 800°C (1472°F)
4 pcf. density @ 1000°C (1832°F)
0.06 (.416)
-
0.11 (.763)
-
0.06 (.416)
-
0.11 (.763)
0.16 (1.11)
-
-
0.11 (.763)
0.16 (1.11)
6 pcf. density @ 400°C (752°F)
6 pcf. density @ 600°C (1112°F)
6 pcf. density @ 800°C (1472°F)
6 pcf. density @ 1000°C (1832°F)
0.076 (.527)
-
0.14 (.971)
-
0.076 (.527)
-
0.14 (.971)
0.20 (1.39)
-
-
0.14 (.971)
0.20 (1.39)
8 pcf. density @ 400°C (752°F)
8 pcf. density @ 600°C (1112°F)
8 pcf. density @ 800°C (1472°F)
8 pcf. density @ 1000°C (1832°F)
0.09 (.624)
-
0.176 (1.22)
-
0.09 (.624)
-
0.176 (1.22)
0.22 (1.53)
-
-
0.176 (1.22)
0.22 (1.53)
Spun Ceramic Fiber Blanket Chemical Composition
Chemical Contents
Commercial Grade
High-Purity Grade
Zirconia
Grade
Al2O3
44%
47% - 49%
39% - 40%
SiO2
52%
50-52%
38-45%
ZrO2
-
-
15-17%
Fe2O3
<1.2%
0.2%
0.2%
K2O + Na2O
<0.5%
0.2%
0.2%
Data are avarage results of test conducted under standard procedures and are subject to variation. Results should not be used for specification purposes.
Note: A material safety data sheet is available upon request.
The information, recommendations and opinions set forth herein are offered solely for your consideration, inquiry and verification, and are not, in part or total, to be construed as constituting a warrant or representation for which we assume legale responsibility. Nothing contained herein is to be interpreted as authorization to practice patented invention without a license.