Fiberglass Twisted Rope, Fiberglass Round Packing, and Fiberglass Square Packing.
|
| |
- High temperature pipes insulation and sealing
- Lining for electric wire and cable insulation
- Thermal insulation for coke furnace and cracking ovens
- Door seals for electric stoves and ovens
- Seal for boiler and high temperature gas-tight parts
- Flexible expansion joint
|
 |
|
| Fiberglass Needlemat |
| |
|
Shanghai GongYe FiberGlass needlemat has been specifically developed for use in vehicle exhaust silencer applications. Manufactured from 9 micron filament E-Glass fibers that are specially carded to produce a high volume batt. This is then mechanically needled to bond the fibers, which results in a dimensionally stable mat or felt, possessing excellent thermal and acoustic insulating properties without any chemical binder.
The mechanical bonding system secures the individual fibers thus eliminating fiber loss via the perforated tubes. InterSource needlemat can be supplied pre-rolled as packs on cardboard mandrels, InterSource packs are wrapped in Polythene sleeves for ease of handling and to reduce any irritation from the glass fiber. We also offer a complete cutting and die-cutting service for more complex shapes.
|
|
|
| |
| PROPERTIES OF FIBERGLASS NEEDLEMAT |
| |
| Fiberglass fibers have a minimal amount of surface dressing that is required to assist in processing, this is usually organic i.e. starch or silage and will disappear at temperatures above 200°C. Fiberglass Needlemats are suitable for continuous use at temperatures up to 550°C higher in exhaust applications, however tensile strength continues to reduce noticeably as temperatures increase above 400°C. |
| |
| Fiberglass Tape |
| |
- For industrial thermal insulation
- Pipe and electrical cable lining
- Thermal wrapping for exhaust pipes
- Flange jointing with bolts (ladder tape)
- Shielding against heat radiation
- High temperature oven door curtain
|
 |
|
| |
| Typical Data of Fiberglass |
| |
|
Articles
|
Working Temp
|
Diameter (mm)
|
| Texturized Fiberglass fiber twisted rope |
up 550°C
|
3,4,5,6,8,10,12,14,15,16,18,20,25,30,35,40
|
|
| |
| FiberGlass Braided Packing |
| |
|
Articles
|
Working Temp
|
Diameter (mm)
|
| Texturized Fiberglass fiber round packing |
up 550°C
|
5,6,8,10,12,14,15,16,18,20,25,30,
35,40,45,50
|
|
| |
| Fiberglass Square Packing |
| |
|
The Main Application
- Thermal insulation and sealing for various stove and boiler applications
- Burner, chimney door sealing
- Seal for heat exchanger, kiln car
- Seal or insulation for heat registrant in furnace
- Seal for high temperature valve or pump
|
|
|
Articles
|
Working Temp
|
Diameter (mm)
|
| Texturized Fiberglass fiber twisted square packing |
up 550°C
|
5x5, 6x6, 8x8, 10x10, 12x12, 14x14, 15x15, 16x16, 18x18, 20x20, 25x25, 30x30, 35x35, 40x40, 45x45, 50x50
|
|
| |
| Technical of Fiberglass Needlemat |
| |
|
Fiberglass Needlemat: are resistant to oils, solvents, and most chemicals although contact with hydrofluoric acids. Strong alkalis and live steam should be avoided.
- are non combustible
- have a low thermal conductivity
- Color: White
- Thermal Conductivity: Thermal 0.78 w/mK 300C mean
- Loss on Ignition: <12%
|
|
| |
| Chemical of Fiberglass Needlemat |
| |
|
Fiberglass
|
SiO2 - 54.1% |
Ai2O3- 15.3% |
| CaO - 17.3% |
MgO - 4.7% |
| Na2O - 0.6% |
B2O3 - 8.0% |
|
| |
| Availability of Fiberglass Needlemat |
| |
| Thickness |
4mm
|
6mm
|
9mm
|
12mm
|
18mm
|
25mm
|
| Weight per m2 150kg/m3 |
600
|
900
|
1350
|
1800
|
2700
|
3600
|
| Weight per m2 130kg/m3 |
520
|
780
|
1171
|
1550
|
2340
|
3125
|
| Roll Length |
50
|
50
|
30
|
20
|
15
|
10
|
Density: available in a range of densities from 100-160 kg/m3
Width: 100cm standard (others available on request) |
| Typical Applications of Fiberglass Needlemat - Insulation media for exhaust silencers, Heatshields. |
|
| |
Data are average results of test conducted under standard procedures and are subject to variation. Results should not be used for specification purposes.
Note: A material safety data sheet is available upon request.
The information, recommendations and opinions set forth herein are offered solely for your consideration, inquiry and verification, and are not, in part or total, to be construed as constituting a warrant or representation for which we assume legal responsibility. Nothing contained herein is to be interpreted as authorization to practice patented invention without a license. |
| |
|